Waterborne polyurethane based on AAS-Na and LDMPA
In a recently published paper, aliphatic diamine sulphonate (AAS-Na) and liquefiable dimethylol propionic acid (LDMPA) were used together to synthesise waterborne polyurethane (WPU) with excellent property.
The influence of -COOH/-SO3Na molar ratio on the structure and properties of the waterborne polyurethanes were characterised by IR, particle size analysis, DSC, DMA, apparent viscosity, water absorption, contact angle, tensile and peel strength tests. It was found that with decreasing -COOH/-SO3Na molar ratio from 10:0 to 3:7, the particle size of the waterborne polyurethane emulsion decreased, while the apparent viscosity of the samples increased.
Increasing the storage modulus of the sample
The water absorption of the WPU films decreased, while the contact angle of the films increased. The tensile strength, elongation at break and peel strength of the samples increased. Furthermore, the results of DMA showed that incorporation of AAS-Na increased the storage modulus of the sample. And the results of DSC showed that with decreasing -COOH/-SO3Na molar ratio from 10:0 to 3:7, Tg of soft segment shifted to lower temperature, which indicated that the micro-phase separation degree of the samples increased.
The study is published in: Progress in Organic Coatings Volume 118, May 2018, Pages 116-121.
Understanding Coatings Raw Materials
What are paints and coatings composed of? This efficient reference book offers an optimum overview of the different constituents of the different types of coatings, explaining the chemistry, system and impacts of coating raw materials. That way, newcomers to the field of coatings gain a quick basic knowledge whereas chemists and laboratory assistants will find valuable insights on future trends and developments in the field of raw materials.
You are currently not logged in
To leave a comment, please log in.
There was an error while sending your comment. Please try again.
Your comment was too long. There are a maximum of 2048 symbols allowed!