Vegetable oils influence photocrosslinking of epoxy-based coatings

The influence of vegetable oils on the photocrosslinking of epoxy-based coatings has been studied Source: Mahesh Patil - Fotolia.com

The influence of cashew nut shell oil (CNO), epoxidized soybean oil (ESO), castor oil (CO), and dioctyl phtalate (DOP) on the photocrosslinking kinetics of UV curable mixtures containing an o-cresol novolac epoxy resin (CNE), a bis-cycloaliphatic diepoxide monomer (BCDE), and a triarylsulfonium salt (TAS) as a cationic photoinitiator has been studied. The formulation with a weight ratio CNE/BCDE/TAS of 60/40/5 was found to have the highest cure rate and the greatest final conversion of epoxy groups upon UV exposure. The presence of an unsaturated oil or of DOP in the UV curable formulation, at a content ranging from 0.07 to 0.79 mol/kg, was shown to increase the initial polymerization rate of the epoxy groups from 12 up to 31 mol/kg s, and the epoxy conversion after 18 s UV exposure from 80 up to 95 %. It was found that the UV cured coatings containing CNO or DOP at concentrations between 0.3 and 0.6 mol/kg and ESO at concentrations between 0.12 and 0.19 mol/kg exhibit the best performance. The materials produced under the optimal conditions determined in this study can be used as high performance decorative and protective coatings and also as adhesives in different sectors of applications.